Formation mechanism of NbC precipitates in micro-alloyed Nb high-strength steel

HU Junjie; REN Ying; ZHANG Lifeng

doi:10.13374/j.issn2095-9389.2022.07.21.001

Volume 45 Issue 10

Oct. 2023

Turn off MathJax

Article Contents

Article Navigation > Chinese Journal of Engineering > 2023 > 45(10): 1729-1739

HU Junjie, REN Ying, ZHANG Lifeng. Formation mechanism of NbC precipitates in micro-alloyed Nb high-strength steel[J]. Chinese Journal of Engineering, 2023, 45(10): 1729-1739. doi: 10.13374/j.issn2095-9389.2022.07.21.001

Citation:

HU Junjie, REN Ying, ZHANG Lifeng. Formation mechanism of NbC precipitates in micro-alloyed Nb high-strength steel[J]. Chinese Journal of Engineering, 2023, 45(10): 1729-1739. doi: 10.13374/j.issn2095-9389.2022.07.21.001

Citation:

PDF( 2647 KB)

Formation mechanism of NbC precipitates in micro-alloyed Nb high-strength steel

doi: 10.13374/j.issn2095-9389.2022.07.21.001

HU Junjie¹,
REN Ying^{1
,
,},
ZHANG Lifeng^{2
,
,}

1.
School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China
2.
School of Mechanical and Materials Engineering, North China University of Technology, Beijing 100144, China

More Information

Corresponding author: REN Ying, E-mail: yingren@ustb.edu.cn; ZHANG Lifeng, E-mail: zhanglifeng@ncut.edu.cn
Received Date: 2022-07-21
Available Online: 2023-01-12
Publish Date: 2023-10-25

Abstract

Abstract

Microalloying and heat treatment are the most important ways to improve the steel properties . In this study, the precipitation behavior of NbC precipitates with Nb content of 210 × 10^–6, 430 × 10^–6, and 690 × 10^–6 and heat treatment temperature of 1000, 1100, 1200, and 1300 ℃ were investigated. DH980 slab was melted in a silicon–molybdenum heating furnace with different Nb additions. The water-quenched steel samples were heated at different temperature in a furnace. The morphology and chemical composition of inclusions in steel samples were determined using an inclusion analysis system. The main inclusions in the Nb micro-alloyed high-Al high-strength steel were Al₂O₃, MnS, and NbC. The measured diameter of NbC precipitates ranged from 0.7 to 6.0 μm, which mainly concentrated on 1.0–2.0 μm. The precipitation temperature and amount of NbC were calculated using the thermodynamic calculation software Factsage. The initial precipitation temperature of NbC precipitates gradually increased to 1125, 1200, and 1260 ℃ as the Nb content increased from 210 × 10^–6 to 690 × 10^–6, respectively, and the NbC precipitation rate (the ratio of NbC mass to the mass of all inclusions) increased to 0.023%, 0.047%, and 0.076%, respectively. The precipitation temperature of MnS was 1450 ℃, which changed little with the content of Nb. Al₂O₃ was present at the melting temperature of steel. The amount of the precipitated NbC in steel increased with an increase in Nb content and heat treatment temperature. The NbC was dissolved in steel when the heat treatment temperature was 1300 ℃, resulting in a decrease in the precipitation of NbC. The size of the NbC precipitates was mainly influenced by the Nb content, heat treatment temperature, and heating time. With the increase in the initial Nb content, the difference in Nb content between the steel matrix and reaction boundary became larger, the diffusion driving force increased, and thus the size of NbC precipitates increased. The diffusion coefficient of Nb varied with the heat treatment temperature, which was hardly influenced by the Nb content. The diffusion coefficient increased with the increase in temperature, which promoted the diffusion of Nb. Consequently, the size of NbC increased with the temperature increased. The diffusivity of Nb increased with an increase in heating time, which also increased the size of NbC. Therefore, the size of NbC precipitates increased as the Nb content, heat treatment temperature, and heating time increased. A kinetic model of NbC precipitation in high-Al high-strength steel was developed to predict the effects of Nb content, heat treatment temperature, and heating time on the size of NbC precipitates.
- high-strength steel,
- Nb micro-alloying,
- heat treatment,
- NbC precipitate,
- kinetics

FullText(HTML)

References(32)

References

[1]	劉清梅, 封嬌潔. 汽車輕量化條件下先進高強鋼的發展及現狀. 軋鋼, 2020, 37(4):65 Liu Q M, Feng J J. Development and current situation of advanced high-strength steel under the condition of automobile light weight. Steel Roll, 2020, 37(4): 65
[2]	王海東, 嚴江生. 淺談先進高強鋼發展現狀與工程創新. 冶金設備, 2021(5):51 Wang H D, Yan J S. Present development and engineering innovation of advanced high strength steel. Metall Equip, 2021(5): 51
[3]	杜一飛, 黎旺, 田亞強. Nb、V、Ti微合金化在汽車用TRIP鋼中的應用進展. 金屬熱處理, 2019, 44(8):50 Du Y F, Li W, Tian Y Q. Application progress of Nb, V and Ti microalloying in TRIP steel for automobile. Heat Treat Met, 2019, 44(8): 50
[4]	張朝磊, 邵洙浩, 李戩, 等. 鈮微合金化技術在中高碳鋼中的應用現狀與發展. 材料導報, 2021, 35(5):5102 Zhang C L, Shao Z H, Li J, et al. Application and development of niobium microalloying technology in medium and high carbon steel. Mater Rep, 2021, 35(5): 5102
[5]	魯達, 李維福, 任英, 等. 固態鋼加熱過程中非金屬夾雜物轉變研究進展. 鋼鐵研究學報, 2020, 32(12):1021 Lu D, Li W F, Ren Y, et al. Transformation of non-metallic inclusions in solid steel during heating process. J Iron Steel Res, 2020, 32(12): 1021
[6]	吳坤. 建筑結構用高強度鋼材力學性能分析. 建材發展導向(上), 2021, 19(1):119 Wu K. Mechanical properties analysis of high strength steel for building structure. Dev Guide Build Mater, 2021, 19(1): 119
[7]	張立峰. 鋼中非金屬夾雜物. 北京: 冶金工業出版社, 2019 Zhang L F. Non-Metallic Inclusions in Steel. Beijing: Metallurgical Industry Press, 2019
[8]	劉城城, 張立峰, 任英, 等. 非金屬夾雜物對不銹鋼耐點蝕性能影響的綜述. 鋼鐵研究學報, 2021, 33(10):1040 Liu C C, Zhang L F, Ren Y, et al. Review on effect of non-metallic inclusions on pitting corrosion resistance of stainless steel. J Iron Steel Res, 2021, 33(10): 1040
[9]	李明, 張立峰, 羅艷, 等. 取向硅鋼連鑄坯中夾雜物和析出相的形貌特征. 中國冶金, 2018, 28(增刊1): 95 Li M, Zhang L F, Luo Y, et al. Morphology of inclusions and precipitates in continuous casting slab of an oriented electrical steel. China Metall, 2018, 28(Sup 1): 95
[10]	石可偉, 蔣棟初, 鄭力寧, 等. 中碳鈮微合金化鋼NbC的析出控制. 連鑄, 2020, 45(3):77 Shi K W, Jiang D C, Zheng L N, et al. Precipitation control of NbC in medium carbon niobium microalloyed steel. Continuous Cast, 2020, 45(3): 77
[11]	Bhattacharyya T, Singh S B, Das S, et al. Development and characterization of C–Mn–Al–Si–Nb TRIP aided steel. Mater Sci Eng A, 2011, 528(6): 2394 doi: 10.1016/j.msea.2010.11.054
[12]	Deng X T, Fu T L, Wang Z D, et al. Extending the boundaries of mechanical properties of Ti–Nb low-carbon steel via combination of ultrafast cooling and deformation during austenite-to-ferrite transformation. Met Mater Int, 2017, 23(1): 175 doi: 10.1007/s12540-017-6241-8
[13]	Esterl R, Sonnleitner M, Schnitzer R. Influences of thermomechanical treatment and Nb micro-alloying on the hardenability of ultra-high strength steels. Metall Mater Trans A, 2019, 50(7): 3238 doi: 10.1007/s11661-019-05235-8
[14]	Funakawa Y, Shiozaki T, Tomita K, et al. Development of high strength hot-rolled sheet steel consisting of ferrite and nanometer-sized carbides. ISIJ Int, 2004, 44(11): 1945 doi: 10.2355/isijinternational.44.1945
[15]	Suzuki H G, Nishimura S, Yamaguchi S. Characteristics of hot ductility in steels subjected to the melting and solidification. Trans Iron Steel Inst Jpn, 1982, 22(1): 48 doi: 10.2355/isijinternational1966.22.48
[16]	Jha G, Das S, Sinha S, et al. Design and development of precipitate strengthened advanced high strength steel for automotive application. Mater Sci Eng A, 2013, 561: 394 doi: 10.1016/j.msea.2012.10.047
[17]	Jung J, Lee S J, Kim S. Effect of Ti additions on micro-alloyed Nb TRIP steel. Steel Res Int, 2011, 82(7): 857 doi: 10.1002/srin.201000273
[18]	Shanmugam S, Tanniru M, Misra R D K, et al. Microalloyed V–Nb–Ti and V steels Part 2–Precipitation behaviour during processing of structural beams. Mater Sci Technol, 2005, 21(2): 165 doi: 10.1179/174328405X18656
[19]	Sobral M, Mei P, Kestenbach H J. Effect of carbonitride particles formed in austenite on the strength of microalloyed steels. Mater Sci Eng A, 2003, 367(1): 317
[20]	DeArdo A J. Metallurgical basis for thermomechanical processing of microalloyed steels. Ironmak Steelmak, 2001, 28(2): 138 doi: 10.1179/030192301678055
[21]	Shibata, Tanaka, Kimura, et al. Composition change in oxide inclusions of stainless steel by heat treatment. Ironmak Steelmak, 2010, 37(7): 522 doi: 10.1179/030192310X12700328925903
[22]	Jandová D, Kasl J. Effect of heat treatment and microalloying on toughness of cast low carbon steel. Mater Sci Forum, 2005, 531(500-501): 489
[23]	Kheirandish S, Noorian A. Effect of niobium on microstructure of cast AISI H13 hot work tool steel. J Iron Steel Res Int, 2008, 15(4): 61 doi: 10.1016/S1006-706X(08)60145-4
[24]	Pang Q H, Guo J, Li W J, et al. Complex precipitation mechanism of Ti–Nb–V microalloyed bainitic base high strength steel. J Wuhan Univ Technol, 2019, 34(6): 1444 doi: 10.1007/s11595-019-2211-y
[25]	Hong S G, Jun H J, Kang K B, et al. Evolution of precipitates in the Nb–Ti–V microalloyed HSLA steels during reheating. Scr Mater, 2003, 48(8): 1201 doi: 10.1016/S1359-6462(02)00567-5
[26]	Saito G, Sakaguchi N, Ohno M, et al. Effects of fine precipitates on austenite grain refinement of micro-alloyed steel during cyclic heat treatment. ISIJ Int, 2019, 59(11): 2098 doi: 10.2355/isijinternational.ISIJINT-2019-153
[27]	Taniguchi T, Satoh N, Saito Y, et al. Investigation of compositional change of inclusions in martensitic stainless steel during heat treatment by newly developed analysis method. ISIJ Int, 2011, 51(12): 1957 doi: 10.2355/isijinternational.51.1957
[28]	楊作宏, 陳伯春. 談微合金元素Nb、V、Ti在鋼中的作用. 甘肅冶金, 2000, 22(4):20 Yang Z H, Chen B C. Discussion on the role of microalloyed elements Nb, V and Ti in steel. Gansu Metall, 2000, 22(4): 20
[29]	Ren Y, Zhang L F. Effect of Al₂O₃–SiO₂–MnO inclusions on precipitation of MnS in Si–Mn-killed 304 stainless steels. Ironmak Steelmak, 2019, 46(6): 558 doi: 10.1080/03019233.2018.1491170
[30]	Kurokawa S, Ruzzante J, Hey A M, et al. Diffusion of Nb in Fe and Fe alloys. Met Sci, 1983, 17: 433 doi: 10.1179/030634583790420628
[31]	Tibbetts G G. Diffusivity of carbon in iron and steels at high temperatures. J Appl Phys, 1980, 51(9): 4813 doi: 10.1063/1.328314
[32]	Fick A. Ueber diffusion. Ann Der Physik, 1855, 170(1): 59 doi: 10.1002/andp.18551700105