Fabrication of the Sheets for Fe<sub>3</sub>Si Based Alloy

LIN Junpin; ZHONG Taibin; LIN Zhi; CHEN Guoliang

doi:10.13374/j.issn1001-053x.2001.05.015

Volume 23 Issue 5

Aug. 2021

Turn off MathJax

Article Contents

Article Navigation > Chinese Journal of Engineering > 2001 > 23(5): 442-444

LIN Junpin, ZHONG Taibin, LIN Zhi, CHEN Guoliang. Fabrication of the Sheets for Fe3Si Based Alloy[J]. Chinese Journal of Engineering, 2001, 23(5): 442-444. doi: 10.13374/j.issn1001-053x.2001.05.015

Citation:

LIN Junpin, ZHONG Taibin, LIN Zhi, CHEN Guoliang. Fabrication of the Sheets for Fe₃Si Based Alloy[J]. Chinese Journal of Engineering, 2001, 23(5): 442-444. doi: 10.13374/j.issn1001-053x.2001.05.015

LIN Junpin, ZHONG Taibin, LIN Zhi, CHEN Guoliang. Fabrication of the Sheets for Fe3Si Based Alloy[J]. Chinese Journal of Engineering, 2001, 23(5): 442-444. doi: 10.13374/j.issn1001-053x.2001.05.015

Citation:

PDF( 529 KB)

Fabrication of the Sheets for Fe₃Si Based Alloy

doi: 10.13374/j.issn1001-053x.2001.05.015

The State Key Laboratory for Advanced Metal Materials, UST Beijing. Beijing 100083, China

Received Date: 2001-02-22

Abstract

Abstract

Based on the Peng's and Chen's works, finding the appropriate technical parameters for forging and rolling, Fe₃Si based alloy sheets of about 1.5 mm in thickness were obtained successfully by the traditional forging and double warm rolling. The grains of the cast structure are larger and not uniform. The uniform tine equiaxed grains form by recrystallization of forging structure. The microstructure becomes elongated after rolling.
- Fe₃Si based alloy,
- warm rolling,
- recrystallization