Changes of Magnetic Properties and Microstructure of NdFeB Ternary System Alloys during Annealing Process

Zhou Shouzeng; Gao Xiaomin; Zhu Jianqing; Qian Xiangrong

doi:10.13374/j.issn1001-053x.1988.04.027

Volume 10 Issue 4

Nov. 2021

Turn off MathJax

Article Contents

Article Navigation > Chinese Journal of Engineering > 1988 > 10(4): 440-446

Zhou Shouzeng, Gao Xiaomin, Zhu Jianqing, Qian Xiangrong. Changes of Magnetic Properties and Microstructure of NdFeB Ternary System Alloys during Annealing Process[J]. Chinese Journal of Engineering, 1988, 10(4): 440-446. doi: 10.13374/j.issn1001-053x.1988.04.027

Citation:

Zhou Shouzeng, Gao Xiaomin, Zhu Jianqing, Qian Xiangrong. Changes of Magnetic Properties and Microstructure of NdFeB Ternary System Alloys during Annealing Process[J]. Chinese Journal of Engineering, 1988, 10(4): 440-446. doi: 10.13374/j.issn1001-053x.1988.04.027

Citation:

PDF( 1226 KB)

Changes of Magnetic Properties and Microstructure of NdFeB Ternary System Alloys during Annealing Process

doi: 10.13374/j.issn1001-053x.1988.04.027

Received Date: 1987-11-17
Available Online: 2021-11-15

Abstract

Abstract

Under temperatures (773~1023K), the results show that in early stage of annealing the coercivity increases sharply and after a peak value, it decrease again. The coercivity for the specimens under annealing state was enhanced one time compared with that of the sintered state. The matrix phase was single phase, in which no crystalline defect was found and the matrix phase was unchanged, only the grain boundaries change. The increase of the coercivity ofter annealing was connected with the changes of grain boundaries.
- rare earth magnet,
- microstructure,
- coercive torce