MgO含量對CaO-SiO₂-Al₂O₃-MgO熔渣中液態相影響的模擬

doi: 10.13374/j.issn1001-053x.2014.s1.029

林騰昌^1,2, ,,
朱榮^1,2,
王成杰^1,2,
李超^1,2,
李明鋼^1,2

1. 北京科技大學鋼鐵冶金新技術國家重點實驗, 北京 100083;
2. 北京科技大學冶金與生態工程學院, 北京 100083

詳細信息

通訊作者:
林騰昌,E-mail:lintengchang@126.com

中圖分類號: TF524
計量
- 文章訪問數: 296
- HTML全文瀏覽量: 94
- PDF下載量: 9
- 被引次數: 0
出版歷程
- 收稿日期: 2013-11-20
- 網絡出版日期: 2021-07-19

Simulation on influence of MgO content on liquid phase in CaO-SiO₂-Al₂O₃-MgO slag

LIN Teng-chang^{1,2
, ,},
ZHU Rong^1,2,
WANG Cheng-jie^1,2,
LI Chao^1,2,
LI Ming-gang^1,2

1. State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China;
2. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China

摘要

摘要: 運用Factsage軟件模擬了MgO含量對CaO-SiO₂-Al₂O₃-MgO熔渣中液相區的影響.結果表明，隨著CaO-SiO₂-Al₂O₃-MgO渣中MgO含量增加，渣中低熔點液相區整體向低CaO高SiO₂區移動.相圖中1500℃液相區比例由0%MgO（質量分數）時的25.05%上升至9%MgO（質量分數）時的52.69%，而后降至15%MgO時的46.70%.相圖中1400℃液相區比例由3%MgO時的14.41%上升至11%MgO時的34.39%，而后降至15%MgO時的31.04%.相圖中1300℃液相區比例由5%MgO時的5.57%上升至14%MgO時的11.02%，而后降至15%MgO時的10.50%.相圖中1200℃液相區域比例在MgO為0~6%時為零，由7%MgO時的0.88%上升至11%MgO時的1.22%，在MgO為13%~15%時降為零.模擬結果可對以CaO-SiO₂-Al₂O₃-MgO為基本組元配置煉鋼渣系的成分選擇提供有效指導.
- CaO-SiO₂-Al₂O₃-MgO熔渣 /
- MgO /
- 液相區
Abstract: The influence of MgO content on liquid phase in CaO-SiO₂-Al₂O₃-MgO slag system was simulated by Factsage software.The results show that,with increase of MgO content in CaO-SiO₂-Al₂O₃-MgO slag,the low melting point liquid area moves forward ‘low CaO high SiO₂’ area. 1500℃ liquid area ratio of phase diagram rises from 25.05% of 0% MgO(mass fraction) to 52.69% of 9% MgO,and drops to 46.70% of 15% MgO. 1400℃ liquid area ratio of phase diagram rises from 14.41% of 3% MgO to 34.39%of 11% MgO,and drops to 31.04% of 15% MgO. 1300℃ liquid area ratio of phase diagram rises from 5.57% of 5% MgO to 11.02% of 14% MgO,and drops to 10.05% of 15% MgO. 1200℃ liquid area ratio of phase diagram is 0 when MgO content during 0 to 6%,and rises from 0.88% of 7% MgO to 1.22% of 11% MgO,then changes to 0 when MgO content during 13% to 15%.Simulation results provide an effective guidance for composition selection of steelmaking slag with the CaO-SiO₂-Al₂O₃-MgO components as the basic configuration.
- CaO-SiO₂-Al₂O₃-MgO slag /
- MgO /
- liquid region