Ni-Cr-Mo-Cu-Mx合金耐晶間腐蝕及點蝕性能

楊瑞成; 牛紹蕊; 李智; 靳塞特

doi:10.13374/j.issn1001-053x.2010.04.009

留言板

尊敬的讀者、作者、審稿人, 關于本刊的投稿、審稿、編輯和出版的任何問題, 您可以本頁添加留言。我們將盡快給您答復。謝謝您的支持!

姓名

郵箱

手機號碼

標題

留言內容

驗證碼

Ni-Cr-Mo-Cu-Mx合金耐晶間腐蝕及點蝕性能

doi: 10.13374/j.issn1001-053x.2010.04.009

1. 蘭州理工大學甘肅省有色金屬新材料省部共建國家重點實驗室, 蘭州 730050;
2. 蘭州理工大學有色金屬合金及加工教育部重點實驗室, 蘭州 730050

基金項目:

甘肅省有色金屬新材料省部共建國家重點實驗室基金資助項目(No.SKL05011)

詳細信息

作者簡介:
楊瑞成(1946-),男,教授,博士生導師,E-mail:yangruicheng@lut.cn

中圖分類號: TG146.1⁺5;TG113.23⁺1
計量
- 文章訪問數: 306
- HTML全文瀏覽量: 77
- PDF下載量: 5
- 被引次數: 0
出版歷程
- 收稿日期: 2009-07-17

Intergranular corrosion and pitting corrosion resistances of Ni-Cr-Mo-Cu-Mx alloys

1. State Key Laboratory of Gansu Advanced Non-ferrous Metal Materials, Lanzhou University of Technology, Lanzhou 730050, China;
2. Key Laboratory of Non-ferrous Metal Alloys and Processing(Ministry of Education of China), Lanzhou University of Technology, Lanzhou 730050, China

摘要

摘要: 向鎳基耐蝕合金中添加Ti、Fe元素,采用手工電弧爐熔煉制備新型Ni-Cr-Mo-Cu-Mx耐蝕合金,用化學浸泡法、電化學法(極化曲線法、循環伏安法)對其耐晶間腐蝕和耐點蝕能力進行研究.結果表明:在Ni-Cr-Mo-Cu合金中加入Ti元素可以增強其耐晶間腐蝕能力,減弱其耐點蝕的能力;加入Fe元素會降低Ni-Cr-Mo-Cu合金耐晶間腐蝕的能力,但提高該合金耐點蝕的能力;實驗合金晶間腐蝕與點蝕的電化學行為和特征與其浸泡腐蝕的結果是吻合的.
- 鎳基合金 /
- 化學浸泡腐蝕 /
- 電化學腐蝕 /
- 晶間腐蝕 /
- 點蝕
Abstract: Ni-Cr-Mo-Cu-Mx nickel-base corrosion-resistant alloys were prepared by adding Ti and Fe with a manual electro-arc furnace.Intergranular corrosion and pitting corrosion resistances of these alloys were investigated by chemical erosion and electrochemical corrosion techniques(polarization curve methods and cyclic voltammetry).The results showed that the intergranular corrosion resistance of the alloys added Ti increased and the pitting corrosion resistance decreased.Fe addition deteriorated the intergranular corrosion resistance of Ni-Cr-Mo-Cu alloys but improved the pitting corrosion resistance.The electrochemical behaviors and characteristics of intergranular corrosion and pitting corrosion coincided with the results of chemical erosion.
- nickel-base alloy /
- chemical erosion /
- electrochemical corrosion /
- intergranular corrosion /
- pitting corrosion