Some Factors Affecting on the Structure-formation and Mechanical Properties of As-Cast High Toughness Nodular Cast Iron
doi: 10.13374/j.issn1001-053x.1989.06.026
Some Factors Affecting on the Structure-formation and Mechanical Properties of As-Cast High Toughness Nodular Cast Iron
-
摘要: Using sand moulds for step-shape casting tests and different silicon percentage of nodular cast iron it was possible to separate structural variations produced during freezing from those occurring at Ac1 transformation temperature. The results show that an increase in silicon content leading to different variation in the matrix structure> leads to a changing mechanical properties of nodular cast irons. Tensile strength and elongation of obtained as-cast nodular cast iron with the composition of 3.9%C, 3.2%Si, 0.5%Mn are maximum of about 524.5N/mm2 and 19.8% accordingly. In the same nodular cast iron, but only with 0.1% Mn the silicon addition first increases after decreases elongation, impact toughness and hardness. But tensile strength changes to the opposite side.Abstract: Using sand moulds for step-shape casting tests and different silicon percentage of nodular cast iron it was possible to separate structural variations produced during freezing from those occurring at Ac1 transformation temperature. The results show that an increase in silicon content leading to different variation in the matrix structure> leads to a changing mechanical properties of nodular cast irons. Tensile strength and elongation of obtained as-cast nodular cast iron with the composition of 3.9%C, 3.2%Si, 0.5%Mn are maximum of about 524.5N/mm2 and 19.8% accordingly. In the same nodular cast iron, but only with 0.1% Mn the silicon addition first increases after decreases elongation, impact toughness and hardness. But tensile strength changes to the opposite side.
-
Key words:
- cast iron, fcrritic structure /
- thin-wall casting
-
點擊查看大圖
計量
- 文章訪問數: 250
- HTML全文瀏覽量: 58
- PDF下載量: 11
- 被引次數: 0
下載: