摘要: Equilibrium between slag and molten iron at 1600℃ was investigated for the direct alloying of steel with Nb2O6-bearing slag. The activity of niobium oxide in the slag was measured. The αNb2O5 is in the range of 10-2-10-4. TheδNb2O5 is ranged in 100-10-2.Niobium partition decreases with the increase of[Si]% and CaO/SiO2. When α[0] and ΣFeO decrease, niobium partition decreases too. The δNb2o5 and the ratio of γsiO2 to γNb2O5 decrease with the incre-ase of slag basicity. The suitable thermodynamic conditions in direct alloying of steel with Nb2O5-bearing slag have been found.
-
關鍵詞:
- equilibrium /
- slag /
- molten /
- alloying /
- Nb2O5
Abstract: Equilibrium between slag and molten iron at 1600℃ was investigated for the direct alloying of steel with Nb2O6-bearing slag. The activity of niobium oxide in the slag was measured. The αNb2O5 is in the range of 10-2-10-4. TheδNb2O5 is ranged in 100-10-2.Niobium partition decreases with the increase of[Si]% and CaO/SiO2. When α[0] and ΣFeO decrease, niobium partition decreases too. The δNb2o5 and the ratio of γsiO2 to γNb2O5 decrease with the incre-ase of slag basicity. The suitable thermodynamic conditions in direct alloying of steel with Nb2O5-bearing slag have been found.-
Key words:
- equilibrium /
- slag /
- molten /
- alloying /
- Nb2O5
-
點擊查看大圖
計量
- 文章訪問數: 225
- HTML全文瀏覽量: 61
- PDF下載量: 12
- 被引次數: 0
下載: