Crystallization kinetics and process of the glass-ceramic produced by nickel slag

MA Mingsheng; NI Wen; WANG Yali

doi:10.13374/j.issn1001-053x.2007.02.040

Volume 29 Issue 2

Aug. 2021

Turn off MathJax

Article Contents

Article Navigation > Chinese Journal of Engineering > 2007 > 29(2): 168-172

MA Mingsheng, NI Wen, WANG Yali. Crystallization kinetics and process of the glass-ceramic produced by nickel slag[J]. Chinese Journal of Engineering, 2007, 29(2): 168-172. doi: 10.13374/j.issn1001-053x.2007.02.040

Citation:

MA Mingsheng, NI Wen, WANG Yali. Crystallization kinetics and process of the glass-ceramic produced by nickel slag[J]. Chinese Journal of Engineering, 2007, 29(2): 168-172. doi: 10.13374/j.issn1001-053x.2007.02.040

Citation:

PDF( 956 KB)

Crystallization kinetics and process of the glass-ceramic produced by nickel slag

doi: 10.13374/j.issn1001-053x.2007.02.040

Civil and Environmental Engineering School, University of Science and Technology Beijing, Beijing 100083, China

Received Date: 2006-09-08
Rev Recd Date: 2006-11-08

Available Online: 2021-08-16

Abstract

Abstract

The glass-ceramic was produced by nickel slag as primary raw material. The crystallization process of the glass-ceramic was analyzed and the crystallization temperature was determined by DSC. The activation E and crystallization kinetic parameter k (T_p) of the glass added 2% Cr₂O₃ by weight as nucleation agent were calculated by the modified Johnson-Mehl-Avrami (JMA) method, and the results were 371. 1 kJ· mol^-1 and 0.29, respectively. The characters of crystals appearing in glass were analyzed by XRD, SEM and optical microscope observation methods. It is shown that the crystallization process is observed between 930℃ and 950℃, and the size of crystals is 10~15μm after heat treatment at 950℃ for 30 min.
- nickel slag,
- glass-ceramic,
- crystallization process,
- kinetic parameter